Composition 100% PES
Basis weight 300 g/m² ± 5%
Width 142 cm ± 3 cm
Abrasion resistance Category A (60 000 strokes)

Composition 100% PES
Basis weight 495 g/m2 +/- 5%
Width 142 cm +/- 3 cm

Fabric type| boucle fabric
Composition| 45% cotton, 40% polyacrylonitrile, 10% poliester, 5% viscose
Weight| 545 g/m² ± 5%
Width| 140 cm ± 2 cm

Grammage m2 220g/m² +/-10%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 25000-30000
Thread displacement 3,1-3,4 mm WARP / 3,8-4,2 mm WEFT
Pilling resistance 5
Fastness to rubbing dry 5
Fastness to rubbing wet 4-5

Fabric type| bouclé fabric
Composition| 54% polyester, 46% polypropylen
Weight| 380 g/m² ± 5%
Width| 145 cm ± 2 cm

Type| chenille fabric
Composition| 100 % polyester
Weight| 585 g/m² ± 5%
Szerokość| 142 cm ± 2 cm
Martindale Abrasion| > 70 000 cycles

Grammage m2 430 g/m² +/-5%

Composition 100% Polyester

Usable width min. 140cm

Martindale Test 130000

Thread displacement 1,0-1,2 mm WARP / 1,0-1,2 mm WEFT

Pilling resistance 4-5

Fastness to rubbing dry 4-5

Fastness to rubbing wet 4-5

Fabric type| knitted fabric
Composition| 100% Polyester
Weight| 350 g/m² ± 5%
Width| 140 cm ± 2 cm

Grammage m2 360g/m² +/-5%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 70000-80000
Thread displacement 2,2-2,4 mm WARP / 1,9-2,1 mm WEFT
Pilling resistance 4
Fastness to rubbing dry 5
Fastness to rubbing wet 5

Fabric type| velvet fabric
Composition| 100% Polyester
Weight| 414 g/m² ± 5%
Width| 142 cm ± 2 cm

Upholstered furniture is not just a component of our interiors, but also an
interesting way to express our style. Looking for the latest trends, it is
worth having a closer look at the Milton collection which offers a range of
stylish colours, enriched with innovative, opalescent texture. The colours of
the knitted fabrics are selected to ensure creative freedom of fabric
combination retaining aesthetic cohesion. A strength of the Milton New fabrics
is their innovative water-repellent quality.

Fabric type| Knitted fabric
---|---
Composition| 97% Polyester, 3% Nylon
Weight| 300 g/m² ± 5%
Width| 140 cm ± 2 cm
Seam slippage| warp 3 mm / warp 4 mm
Martindale abrasion| 90 000 cycles
Colour fastness test| dry 4-5 / wet 4
Tear strenght| warp 160 N / weft 49 N
Tensile strenght| warp 1000 N / weft 840 N
Colour fastness to light| 4
Pilling| 5
Fire resistance| BS 5852: Part 1: 1979, source 0 (cigarette)

Width| 315 cm
Composition| 100% polyester

Grammage m2 410g/m² +/-10%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 25000-30000
Thread displacement 1,7-2,2 mm WARP / 2,0-2,6 mm WEFT
Pilling resistance 4-5
Fastness to rubbing dry 5
Fastness to rubbing wet 4-5

Composition 100% PES
Basis weight 450 g/m2 ± 5%
Width 142 ± 3 cm
Abrasion resistance 90 000 rubs (cat. A)

Composition| 80% Polyester, 20% Cotto

Fabric type| Chenille fabric
Composition| 100% polyester
Weight| 470 g/m² ± 5%
Width| 142 cm ± 2 cm
Martindale abrasion| > 40 000 cycles

Width| 300 cm ± 1 cm
Composition| 82% wool, 18% acrylic
Weight| 130 g/m² ± 5%
Shrinkage| 5%

# Grammage m2 380g/m² +/-5%

# Composition 100% Polyester

# Usable width min. 140cm

# Martindale Test 80000-90000

# Thread displacement 2,1-2,5 mm WARP / 1,4-1,6 mm WEFT

# Pilling resistance 4-5

# Fastness to rubbing drylight-4-5 / medium-4-5 / dark-4-5

# Fastness to rubbing wetlight-4-5 / medium-4-5 / dark-4-5

Fabric type| woven fabric
Composition| 36% polyester, 41% acrylic, 18% viscose, 5% linen
Weight| 600 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 60 000 cycles

Type| bouclé fabric
Composition| 100 % polyester
Weight| 800 g/m² ± 3%
Width| 140 cm ± 2 cm
Martindale Abrasion| > 25 000 cycles

Grammage m2 330g/m² +/-5%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test >100000
Thread displacement 2,6-2,9 mm WARP / 2,8-3,2 mm WEFT
Pilling resistance 5
Fastness to rubbing dry 5
Fastness to rubbing wet 3-4