Fabric type| chenille fabric
Composition| 100 % polyester
Weight| 510 g/m² ± 5%
Width| 142 cm ± 2 cm
Martindale abrasion| > 50 000 cycles

Grammage m2 420g/m² +/-5%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 90000-100000
Thread displacement 1,9-2,1 mm WARP / 1,5-1,7 mm WEFT
Pilling resistance 4
Fastness to rubbing dry 4-5
Fastness to rubbing wet 4-5

Width| 290 cm ± 1 %
Composition| 100% polyester
Weight| 79 g/m² ± 5%

Fabric type| bouclé fabric
Composition| 80% acrylic, 15% poliester, 5% linen
Weight| 571 g/m² ± 5%
Width| 140 cm ± 2 cm

Grammage m2 450g/m² +/-5%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 140000
Thread displacement 1,7-1,9 mm WARP / 1,9-2,1 mm WEFT
Pilling resistance 4-5
Fastness to rubbing dry 4-5
Fastness to rubbing wet 4-5

Composition 100% PES
Basis weight 420 g/m2 +/- 5%
Width 142 cm +/- 3 cm
Abrasion resistance 25 000 (rubs)[
Atest papierosa

Fabric type| woven fabric
Composition| 54% rolefin, 29% polyacrylonitrile, 17% polyester
Weight| 562 g/m² ± 5%
Width| 145 cm ± 2 cm
Martindale abrasion| > 45 000 cycles

Fabric type| chenille fabric
Composition| 100% polyester
Weight| 409 g/m² ± 5%
Width| 140 cm ± 2 cm
Seam slippage| warp 3-4 / weft 2-3
Martindale abrasion| 90 000 cycles

Composition 100% PES
Basis weight 320 g/m² ± 5 %
Width 142 ± 3 cm
Abrasion resistance 50 000 cycles (category A)

Width| 320 cm ± 1%
Composition| 100% polyester
Weight| 81 g/m² ± 5%
Shrinkage| 1%

Fabric type| woven fabric
Composition| 100% recycled polyester
Weight| 318 g/m² ± 5%
Width| 140 cm ± 2 cm
Seam slippage| weft 4,2 mm / warp 3,7 mm
Martindale abrasion| 40 000 cycles

Width| 298 cm ± 1%
Composition| 50% linene, 30% polyester, 19% viscose, 1% polyamide
Weight| 169 g/m² ± 5%

Composition 100% PES
Basis weight 260 g/m² ±
Width 142 ± 3 cm 5%
Abrasion resistance 45 000 strokes (rubs)

Fabric type| chenille fabric
Composition| 47% Polyester, 45% Polyamide, 8% Viscose
Weight| 410 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 35 000

Fabric type| chenille fabric
Composition| 56% acrylic, 39% polyester, 5% viscose
Weight| 465 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 35 000 cycles

Grammage m2 330g/m2 +/- 5%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 45000-55000
Thread displacement 0,9-1,1 mm WARP / 1,4-1,6 mm WEFT
Pilling resistance 4-5
Fastness to rubbing drylight 5 / medium 4-5 / dark 5
Fastness to rubbing wetlight 5 / medium 4-5 / dark 4-5

Fabric type| velvet fabric
Composition| 100% polyester
Weight| 360 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 75 000 cycles

Width| 280 cm
Composition| 100% polyester
Weight| 250 g/m² ± 5%
Shrinkage| 2%
Fire retardant| BS 5852: Part 1: 1979, Ignition source 0 (Cigarette

Fabric type| chenille fabric
Composition| 52% polyester, 23% cotton, 13% linen,
12% viscose
Weight| 350 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 35 000 cycles

Composition 100% PES
Basis weight 450 g/m² ± 5%
Width 142 ± 3 cm
Abrasion resistance Category A (90 000 strokes)

Fabric type| knitted fabric
Composition| 100% Polyester
Weight| 350 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 45 000 cycles

Grammage m2 330g/m² +/-5%
Composition 94% Polyester 6% Nylon
Usable width min. 140cm
Martindale Test 25000-35000
Thread displacement 3,6-4,0 mm WARP / 3,1-3,5 mm WEFT
Pilling resistance 5
Fastness to rubbing dry 4-5
Fastness to rubbing wet 4-5

Fabric type| Eco leather PU
Composition| 65% Polyurethane, 21% Polyester, 14% Cotton
Weight| 480 g/m² ± 5%
Width| 137 cm ± 2 cm
Thickness| 0,9 ± 0,05 mm
Martindale abrasion| > 50 000 cycles

Fabric type| chenille fabric
Composition| 52% polyester, 23% cotton, 13% linen,
12% viscose
Weight| 350 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 35 000 cycles

Width| 287 cm ± 1 %
Composition| 100% linen
Weight| 149 g/m² ± 5%

Fabric type| boucle fabric
Composition| 49% Polyester, 40% Acrylic, 11% Viscose
Weight| 660 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 35 000 cycles

Fabric type| knitted velvet
Composition| 100% Polyester
Weight| 400 g/m² ± 5%
Width| 140 cm ± 2 cm
Martindale abrasion| 70 000 cycles

Grammage m2 230g/m² +/-5%
Composition 100% Polyester
Usable width min. 140cm
Martindale Test 30000-40000
Thread displacement 2,8-3,2 mm WARP / 2,9-3,3 mm WEFT
Pilling resistance 4-5
Fastness to rubbing dry 4-5
Fastness to rubbing wet 4

Composition 100% PES
Basis weight 380 g/m2 +/- 5%
Width 142 cm +/- 3 cm
Abrasion resistance 80 000 suwów (rubs)